SPECIFICATION
Supplier : Samsung electro-mechanics Samsung P/N : CL32A106KOCLNWE
Product : Multi-layer Ceramic Capacitor Description : CAP, 10㎌, 16V, ±10%, X5R, 1210
CL 32 A106 K O C L N W E
① ②③ ④ ⑤⑥⑦⑧⑨⑩⑪
①Series Samsung Multi-layer Ceramic Capacitor
②Size 1210 (inch code) L: 3.2 ± 0.3 mm W: ± 0.2 mm
⑧Thickness division Low profile
③Dielectric X5R Inner electrode
④Capacitance 10 ㎌Termination
⑤Capacitance ±10 % Plating (Pb Free)
tolerance ⑨Product Normal
⑥Rated Voltage 16 V ⑩Special Product for Network application
⑦Thickness 0.85 ± 0.1 mm ⑪Packaging Embossed Type, 7"reel(2,000ea)
A. Samsung Part Number
Sn 100%
Cu
Ni
2.5
B. Samsung Reliability Test and Judgement condition
Capacitance Within specified tolerance 1㎑±10% 1.0±0.2 Vrms
Tan δ (DF) 0.1 max.
Insulation More than 100Mohm㎌Rated Voltage 60~120 sec.
Resistance
Appearance No abnormal exterior appearance Visual inspection
Withstanding No dielectric breakdown or of the rated voltage
Voltage mechanical breakdown
Temperature X5R
Characteristics (From -55℃ to 85℃, Capacitance change should be within ±15%)
Adhesive Strength No peeling shall be occur on the 500gF, for 10±1 sec.
of Termination terminal electrode
Bending Strength Capacitance change : within ±12.5% Bending to the limit (1mm)
with 1.0mm/sec.
Solderability More than 75% of terminal surface SnAg3.0Cu0.5 solder
is to be soldered newly 245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to Capacitance change : within ±7.5% Solder pot : 270±5℃, 10±1sec.
Soldering heat Tan δ, IR : initial spec.
250%
Performance Test condition
Vibration Test Capacitance change : within ±5% Amplitude : 1.5mm
Tan δ, IR : initial spec. From 10㎐ to 55㎐ (return : 1min.)
2hours 3 direction (x, y, z)
Moisture Capacitance change : within ±12.5% With rated voltage
Resistance Tan δ : 0.125 max 40±2℃, 90~95%RH, 500+12/-0 hours
IR : More than 12.5㏁·㎌
High Temperature Capacitance change : within ±12.5% Wit
h
of the rated voltage
Resistance Tan δ : 0.125 max Max. operating temperature
IR : More than 25㏁·㎌
1000+48/-0 hours
Temperature Capacitance change : within ±7.5% 1 cycle condition
Cycling Tan δ, IR : initial spec. Min. operating temperature →25℃
→Max. operating temperature →25℃
5 cycles test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.
Performance Test condition
150%